Milling inserts
Milling inserts OFMT
Properties and application:
- Carbide insert, grade PL 30, PVD coating (TiAlN)
- 43° milling
- Technical information on DARMET inserts
Specifications:
 |
||
| Insert shape and angle | ||
|---|---|---|
| O | 135° |  |
| Normal clearance angle | ||
| F | 25° |  |
| Tolerance class | ||
| M | l ? 0,05 m ? 0,013 s ? 0,025 |
 |
| Chipbreaker and clamping type | ||
| T |  |
|
 |
 |
 |
| To increase productivity it is recommended to increase feed while respecting cutting speed | Please use coolant when machining suitable material groups | Respect recommended cutting speed during stainless steel machining |
| Operations | |
|---|---|
 |
 |
| Surfacing | Chamfering |
| Designation | Grade | l | s | P/r | D | Cutting direction |
|---|---|---|---|---|---|---|
| OFMT 05T305 TN | PL 30 | 5 | 3,97 | 0,8 | - | right |
| OFMT 050405 TR | PL 30 | 5 | 4,76 | 0,8 | - | right |
| OFMT 070405 TN | PL 30 | 7 | 4,76 | 0,8 | - | right |
| OFMT 05T305 TN i OFMT 050405 TR | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 3,5 | 0,23 | 0,48 | 190 | 350 |
| 180 | 3,5 | 0,48 | 300 | |||||
| 210 | 3,5 | 0,48 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 3,5 | 0,28 | 0,42 | 150 | 240 |
| 230 | 3,5 | 0,42 | 210 | |||||
| 280 | 0,5 | 3,5 | 0,28 | 0,35 | 130 | 190 | ||
| 320 | 3,5 | 0,35 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 3,5 | 0,15 | 0,32 | 90 | 150 |
| 280 | 3,5 | 0,32 | 130 | |||||
| 320 | 0,5 | 3,5 | 0,15 | 0,28 | 60 | 110 | ||
| 350 | 3,5 | 0,28 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 3,5 | 0,22 | 0,35 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 3,5 | 0,18 | 0,32 | 160 | 210 | |
| 6 | - | 0,5 | 3,5 | 0,15 | 0,28 | 70 | 150 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 3,5 | 0,18 | 0,35 | 150 | 210 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 3,5 | 0,18 | 0,35 | 150 | 230 |
| treated | 0,5 | 3,5 | 0,18 | 0,28 | 90 | 170 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 3,5 | 0,20 | 0,50 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 3,5 | 0,18 | 0,48 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | 0,5 | 3,5 | 0,15 | 0,30 | 25 | 35 |
| 28 | 40 | |||||||
| 40 | 60 | |||||||
| Titanium based alloys |
12 | - | 0,5 | 3,5 | 0,15 | 0,35 | 35 | 60 |
| 0,28 | 28 | 40 | ||||||
| OFMT 070405 TN | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 4,5 | 0,23 | 0,48 | 190 | 350 |
| 180 | 4,5 | 0,48 | 300 | |||||
| 210 | 4,5 | 0,48 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 4,5 | 0,28 | 0,42 | 150 | 240 |
| 230 | 4,5 | 0,42 | 210 | |||||
| 280 | 0,5 | 4,5 | 0,28 | 0,35 | 130 | 190 | ||
| 320 | 4,5 | 0,35 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 4,0 | 0,15 | 0,32 | 90 | 150 |
| 280 | 4,0 | 0,32 | 130 | |||||
| 320 | 0,5 | 4,0 | 0,15 | 0,28 | 60 | 110 | ||
| 350 | 4,0 | 0,28 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 4,5 | 0,22 | 0,35 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 4,5 | 0,18 | 0,32 | 160 | 210 | |
| 6 | - | 0,5 | 4,5 | 0,15 | 0,28 | 70 | 150 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 4,5 | 0,18 | 0,35 | 150 | 210 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 4,5 | 0,18 | 0,35 | 150 | 230 |
| treated | 0,5 | 4,5 | 0,18 | 0,28 | 90 | 170 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 4,5 | 0,20 | 0,50 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 4,0 | 0,18 | 0,48 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | 0,5 | 4,0 | 0,15 | 0,30 | 25 | 35 |
| 28 | 40 | |||||||
| 40 | 60 | |||||||
| Titanium based alloys |
12 | - | 0,5 | 4,0 | 0,15 | 0,35 | 35 | 60 |
| 0,28 | 28 | 40 | ||||||
Milling inserts OFER
Properties and application:
- Carbide insert, grade PL 30, PVD coating (TiAlN)
- 43° milling
- Technical information on DARMET inserts
Specifications:
 |
||
| Insert shape and angle | ||
|---|---|---|
| O | 135° | |
| Normal clearance angle | ||
| F | 25° | |
| Tolerance class | ||
| E | l ? 0,025 m ? 0,025 s ? 0,025 |
|
| Chipbreaker and clamping type | ||
| R |  |
|
|
|
|
| To increase productivity it is recommended to increase feed while respecting cutting speed | Please use coolant when machining suitable material groups | Respect recommended cutting speed during stainless steel machining |
| Operations | |
|---|---|
|
|
| Surfacing | Chamfering |
| Designation | Grade | l | s | P/r | D | Cutting conditions |
|---|---|---|---|---|---|---|
| OFER 070405 TN | PL 30 | 5 | 4,76 | 0,8 | - | right |
| OFER 070405 TN | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 4,0 | 0,18 | 0,32 | 190 | 350 |
| 180 | 4,0 | 0,32 | 300 | |||||
| 210 | 4,0 | 0,32 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 4,0 | 0,15 | 0,30 | 150 | 240 |
| 230 | 4,0 | 0,30 | 210 | |||||
| 280 | 0,5 | 4,0 | 0,15 | 0,30 | 130 | 190 | ||
| 320 | 4,0 | 0,30 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 4,0 | 0,12 | 0,25 | 90 | 150 |
| 280 | 4,0 | 0,25 | 130 | |||||
| 320 | 0,5 | 4,0 | 0,12 | 0,25 | 60 | 110 | ||
| 350 | 4,0 | 0,25 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 5,0 | 0,18 | 0,32 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 5,0 | 0,15 | 0,28 | 160 | 210 | |
| 6 | - | 0,5 | 3,5 | 0,12 | 0,25 | 70 | 150 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 5,0 | 0,12 | 0,32 | 150 | 210 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 5,0 | 0,12 | 0,32 | 150 | 230 |
| treated | 0,5 | 5,0 | 0,12 | 0,25 | 90 | 170 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 5,0 | 0,15 | 0,40 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 5,0 | 0,12 | 0,32 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | 0,5 | 3,5 | 0,12 | 0,28 | 25 | 35 |
| 28 | 40 | |||||||
| 40 | 60 | |||||||
| Titanium based alloys |
12 | - | 0,5 | 3,5 | 0,12 | 0,28 | 35 | 60 |
| 0,28 | 28 | 40 | ||||||
Milling inserts ODMW
Properties and application:
- Carbide insert, grade PL 30, PVD coating (TiAlN)
- 45° milling
- Technical information on DARMET inserts
Specifications:
 |
||
| Insert shape and angle | ||
|---|---|---|
| O | 135° | |
| Normal clearance angle | ||
| D | 15° |  |
| Tolerance class | ||
| M | l ? 0,05 m ? 0,013 s ? 0,025 |
|
| Chipbreaker and clamping type | ||
| W |  |
|
|
|
|
| To increase productivity it is recommended to increase feed while respecting cutting speed | Please use coolant when machining suitable material groups | Respect recommended cutting speed during stainless steel machining |
| Operations | |
|---|---|
|
|
| Surfacing | Chamfering |
| Designation | Grade | l | s | P/r | D | Cutting direction |
|---|---|---|---|---|---|---|
| ODMW 060508 TN | PL 30 | 6 | 5,56 | 0,8 | - | right |
| ODMW 060508 TN | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 4,0 | 0,28 | 0,52 | 190 | 350 |
| 180 | 4,0 | 0,52 | 300 | |||||
| 210 | 4,0 | 0,52 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 4,0 | 0,25 | 0,48 | 150 | 240 |
| 230 | 4,0 | 0,48 | 210 | |||||
| 280 | 0,5 | 4,0 | 0,25 | 0,42 | 130 | 190 | ||
| 320 | 4,0 | 0,42 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 4,0 | 0,23 | 0,38 | 90 | 150 |
| 280 | 4,0 | 0,38 | 130 | |||||
| 320 | 0,5 | 4,0 | 0,23 | 0,32 | 60 | 110 | ||
| 350 | 4,0 | 0,32 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | Not recommended | |||||
| 5 | 230 - 270 | |||||||
| 6 | - | |||||||
| Ferritic stainless steel |
7 | annealed | ||||||
| Martensitic stainless steel |
8 | annealed | ||||||
| treated | ||||||||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 4,0 | 0,25 | 0,6 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 4,0 | 0,23 | 0,5 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | Not recommended | |||||
| Nickel based alloys |
12 | - | ||||||
Milling inserts ODMT
Properties and application:
- Carbide insert, grade PL 30, PVD coating (TiAlN)
- 45° milling
- Technical information on DARMET inserts
Specifications:
 |
||
| Insert shape and angle | ||
|---|---|---|
| O | 135° | |
| Normal clearance angle | ||
| D | 15° | |
| Tolerance class | ||
| M | l ? 0,05 m ? 0,013 s ? 0,025 |
|
| Chipbreaker and clamping type | ||
| T | |
|
|
|
|
| To increase productivity it is recommended to increase feed while respecting cutting speed | Please use coolant when machining suitable material groups | Respect recommended cutting speed during stainless steel machining |
| Operations | |
|---|---|
|
|
| Surfacing | Chamfering |
| Designation | Grade | l | s | P/r | D | Cutting direction |
|---|---|---|---|---|---|---|
| ODMT 0504 ZZTR | PL 30 | 5 | 4,76 | 0,8 | - | right |
| ODMT 060508 TN | PL 30 | 6 | 5,56 | 0,8 | - | right |
| ODMT 0504 ZZTR | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 3,5 | 0,23 | 0,48 | 190 | 350 |
| 180 | 3,5 | 0,48 | 300 | |||||
| 210 | 3,5 | 0,48 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 3,5 | 0,28 | 0,42 | 150 | 240 |
| 230 | 3,5 | 0,42 | 210 | |||||
| 280 | 0,5 | 3,5 | 0,28 | 0,35 | 130 | 190 | ||
| 320 | 3,5 | 0,35 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 3,5 | 0,15 | 0,32 | 90 | 150 |
| 280 | 3,5 | 0,32 | 130 | |||||
| 320 | 0,5 | 3,5 | 0,15 | 0,28 | 60 | 110 | ||
| 350 | 3,5 | 0,28 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 3,5 | 0,22 | 0,35 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 3,5 | 0,18 | 0,32 | 160 | 210 | |
| 6 | - | 0,5 | 3,5 | 0,15 | 0,28 | 70 | 150 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 3,5 | 0,18 | 0,35 | 150 | 210 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 3,5 | 0,18 | 0,35 | 150 | 230 |
| treated | 0,5 | 3,5 | 0,18 | 0,28 | 90 | 170 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 3,5 | 0,20 | 0,50 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 3,5 | 0,18 | 0,48 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | 0,5 | 3,5 | 0,15 | 0,30 | 25 | 35 |
| 28 | 40 | |||||||
| 40 | 65 | |||||||
| Titanium based alloys | 12 | - | 0,5 | 3,5 | 0,15 | 0,35 | 35 | 60 |
| 0,28 | 28 | 40 | ||||||
| ODMT 060508 TN | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/obr.] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 4,0 | 0,18 | 0,32 | 190 | 350 |
| 180 | 4,0 | 0,32 | 300 | |||||
| 210 | 4,0 | 0,32 | 260 | |||||
| Alloy steel | 2 | 180 | 0,5 | 4,0 | 0,15 | 0,30 | 150 | 240 |
| 230 | 4,0 | 0,30 | 210 | |||||
| 280 | 0,5 | 4,0 | 0,15 | 0,30 | 130 | 190 | ||
| 320 | 4,0 | 0,30 | 170 | |||||
| High alloy steel | 3 | 220 | 0,5 | 4,0 | 0,12 | 0,25 | 90 | 150 |
| 280 | 4,0 | 0,25 | 130 | |||||
| 320 | 0,5 | 4,0 | 0,12 | 0,25 | 60 | 110 | ||
| 350 | 4,0 | 0,25 | 90 | |||||
| 400 | 0,5 | 3,0 | 0,14 | 0,25 | 40 | 80 | ||
| 480 | 2,0 | 0,22 | 70 | |||||
| 550 | 1,0 | 0,20 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 4,0 | 0,18 | 0,35 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 4,0 | 0,18 | 0,32 | 160 | 210 | |
| 6 | - | 0,5 | 4,0 | 0,15 | 0,28 | 70 | 150 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 4,0 | 0,21 | 0,38 | 150 | 210 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 4,0 | 0,21 | 0,38 | 150 | 230 |
| treated | 0,5 | 4,0 | 0,21 | 0,32 | 90 | 170 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 4,0 | 0,22 | 0,50 | 170 | 300 |
| 250 | ||||||||
| 210 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 4,0 | 0,18 | 0,45 | 120 | 210 |
| 260 | 170 | |||||||
| 310 | 150 | |||||||
| 450 | 0,5 | 3,0 | 0,14 | 0,25 | 30 | 60 | ||
| Nickel based alloys |
11 | - | 0,5 | 4,0 | 0,16 | 0,32 | 25 | 35 |
| 28 | 40 | |||||||
| 40 | 65 | |||||||
| Titanium based alloys |
12 | - | 0,5 | 4,0 | 0,18 | 0,32 | 35 | 60 |
| 0,28 | 28 | 40 | ||||||
Milling inserts LDMT
Properties and application:
- Carbide insert, grade PL 30, PVD coating (TiAlN)
- 90° milling
- Technical information on DARMET inserts
Specifications:
 |
||
| Insert shape and angle | ||
|---|---|---|
| L | 90° |  |
| Normal clearance angle | ||
| D | 15° | |
| Tolerance class | ||
| M | l ? 0,05 m ? 0,013 s ? 0,025 |
 |
| Chipbreaker and clamping type | ||
| T | |
|
|
|
|
| To increase productivity it is recommended to increase feed while respecting cutting speed | Please use coolant when machining suitable material groups | Respect recommended cutting speed during stainless steel machining |
| Operations | ||
|---|---|---|
 |
 |
|
| Slotting | Shoulder milling | Surfacing |
| Designation | Grade | l | s | P/r | D | Cutting direction |
|---|---|---|---|---|---|---|
| LDMT 1504 PDTR | PL 30 | 15 | 4,76 | 90° | 15° | right |
| LDMT 1504 PDTR | ||||||||
|---|---|---|---|---|---|---|---|---|
| Material group | Group number | Brinell hardness [HB] | ap [mm] | Feed [mm/turn] | Vc [m/min] | |||
| min | max | min | max | min | max | |||
| Low carbon steel | 1 | 150 | 0,5 | 14,0 | 0,10 | 0,38 | 180 | 300 |
| 180 | 14,0 | 0,25 | 260 | |||||
| 210 | 14,0 | 0,23 | 220 | |||||
| Alloy steel | 2 | 180 | 0,5 | 14,0 | 0,08 | 0,22 | 130 | 200 |
| 230 | 14,0 | 0,22 | 180 | |||||
| 280 | 0,5 | 14,0 | 0,08 | 0,18 | 100 | 160 | ||
| 320 | 14,0 | 0,18 | 140 | |||||
| High alloy steel | 3 | 220 | 0,5 | 7,0 | 0,08 | 0,18 | 90 | 130 |
| 280 | 7,0 | 0,18 | 110 | |||||
| 320 | 0,5 | 7,0 | 0,08 | 0,16 | 60 | 100 | ||
| 350 | 7,0 | 0,16 | 90 | |||||
| 400 | 0,5 | 4,0 | 0,10 | 0,16 | 40 | 80 | ||
| 480 | 2,0 | 0,15 | 70 | |||||
| 550 | 1,0 | 0,14 | 60 | |||||
| Austenitic stainless steel |
4 | 210 - 250 | 0,5 | 14,0 | 0,10 | 0,22 | 190 | 250 |
| 5 | 230 - 270 | 0,5 | 14,0 | 0,10 | 0,20 | 160 | 210 | |
| 6 | - | 0,5 | 7,0 | 0,08 | 0,18 | 70 | 120 | |
| Ferritic stainless steel |
7 | annealed | 0,5 | 7,0 | 0,08 | 0,20 | 150 | 230 |
| Martensitic stainless steel |
8 | annealed | 0,5 | 7,0 | 0,08 | 0,20 | 130 | 210 |
| treated | 0,5 | 7,0 | 0,08 | 0,20 | 90 | 150 | ||
| Grey cast iron | 9 | 140 - 230 | 0,5 | 14,0 | 0,10 | 0,25 | 150 | 240 |
| 220 | ||||||||
| 190 | ||||||||
| Nodular cast iron | 10 | 210 | 0,5 | 14,0 | 0,10 | 0,22 | 100 | 200 |
| 260 | 160 | |||||||
| 310 | 130 | |||||||
| 450 | 0,5 | 3,0 | 0,10 | 0,14 | 30 | 60 | ||
| Nickel based alloy |
11 | - | 0,5 | 5,0 | 0,08 | 0,15 | 25 | 35 |
| 28 | 38 | |||||||
| 40 | 65 | |||||||
| Titanium based alloy | 12 | - | 0,5 | 5,0 | 0,08 | 0,18 | 35 | 60 |
| 0,15 | 28 | 40 | ||||||