Properties and application:

Specification:

APLX 
Insert shape and angle
A  85° shape a 85 
Normal clearance angle
P 11° angle p 11 
Tolerance class
L l ? 0,05
m ? 0,013
s ? 0,025
 tolerance sh a 
Chipbreaker and clamping type
X type X

 

productivity feed coolant stainless steel
To increase productivity it is recommended to increase feed while respecting cutting speed Please use coolant when machining suitable material groups Respect recommended cutting speed during stainless steel machining

 

Operations
frezowanie rowkow frezowanie wystepow frezowanie czolowe
Slotting Shoulder milling Surfacing

 

DesignationGradelsP/rDCutting direction
APLX 1003 PDTR PL 30 10 3,18 90° 15° right
APLX 100308 PDTR PL 30 10 3,18 0,8 15° right
APLX 100332 PDTR PL 30 10 3,18 3,2 15° right
APLX 100340 PDTR PL 30 10 3,18 4,0 15° right

 

APLX 1003 PDTR i APLX 100308 PDTR
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]Vc [m/min]
minmaxminmaxminmax
Low carbon steel 1 150 0,5 9,0 0,10 0,38 180 300
180 9,0 0,25 260
210 9,0 0,23 220
Alloy steel 2 180 0,5 9,0 0,08 0,22 130 200
230 9,0 0,22 180
280 0,5 9,0 0,08 0,18 100 160
320 9,0 0,18 140
High alloy steel 3 220 0,5 7,0 0,08 0,18 90 130
280 7,0 0,18 110
320 0,5 7,0 0,08 0,16 60 100
350 7,0 0,16 90
400 0,5 4,0 0,10 0,16 40 80
480 2,0 0,15 70
550 1,0 0,14 60
Austenitic stainless steel
 4 210 - 250 0,5 9,0 0,10 0,22 190 250
5 230 - 270 0,5 9,0 0,10 0,20 160 210
6 - 0,5 9,0 0,08 0,18 70 120
Ferritic stainless steel
 7 annealed 0,5 9,0 0,08 0,20 150 230
Martensitic stainless steel
 8 annealed 0,5 9,0 0,08 0,20 130 210
treated 0,5 9,0 0,08 0,20 90 150
Grey cast iron 9 140 - 230 0,5 9,0 0,10 0,25 150 240
220
190
Nodular cast iron 10 210 0,5 9,0 0,10 0,22 100 200
260 160
310 130
450 0,5 3,0 0,10 0,14 30 60
Nickel based alloys 11 - 0,5 5,0 0,08 0,15 25 35
28 38
40 65
Titanium based alloys
 12 - 0,5 5,0 0,08 0,18 35 60
0,15 28 40

 

APLX 100332 PDTR i APLX 100340 PDTR
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]Vc [m/min]
minmaxminmaxminmax
Low carbon steel 1 150 0,5 9,0 0,18 0,38 180 300
180 9,0 0,25 260
210 9,0 0,23 220
Alloy steel 2 180 0,5 9,0 0,15 0,22 130 200
230 9,0 0,22 180
280 0,5 9,0 0,15 0,18 100 160
320 9,0 0,18 140
High alloy steel 3 220 0,5 7,0 0,12 0,18 90 130
280 7,0 0,18 110
320 0,5 7,0 0,12 0,16 60 100
350 7,0 0,16 90
400 0,5 4,0 0,10 0,16 40 80
480 2,0 0,15 70
550 1,0 0,14 60
Austenitic stainless steel
 4 210 - 250 0,5 9,0 0,10 0,22 190 250
5 230 - 270 0,5 9,0 0,10 0,20 160 210
6 - 0,5 9,0 0,08 0,18 70 120
Ferritic stainless steel
 7 annealed 0,5 9,0 0,08 0,20 150 230
Martensitic stainless steel
 8 annealed 0,5 9,0 0,08 0,20 130 210
treated 0,5 9,0 0,08 0,20 90 150
Grey cast iron 9 140 - 230 0,5 9,0 0,10 0,32 150 240
220
190
Nodular cast iron 10 210 0,5 9,0 0,10 0,28 100 200
260 160
310 130
450 0,5 3,0 0,10 0,14 30 60
Nickel based alloys
 11 - 0,5 5,0 0,08 0,15 25 35
28 38
40 65
Titanium based alloys
 12 - 0,5 5,0 0,08 0,18 35 60
0,15 28 40