Properties and application:

Specifications:

Indexable turning instert CCMT
Insert shape and angle
D 55° shape d 55 
Normal clearance angle
N 0° angle n 0 
Tolerance class
M l ? 0,05
m ? 0,08
s ? 0,13
 tolerance sh d 
Chipbreaker and clamping type
G   type G

 

Insert application guide
Designation Super finishing Finishing Semi finishing Roughing Interrupted cut
DNMG 110404 NN m4 m4 m2 m1 m1
DNMG 110408 NN m2 m4 m3 m3 m2
DNMG 150404 NN m3 m4 m2 m1 m1
DNMG 150408 NN m2 m4 m4 m3 m2
DNMG 150412 NN m1 m3 m4 m4 m4
DNMG 150604 NN m3 m4 m2 m1 m1
DNMG 150608 NN m2 m4 m4 m1 m2
DNMG 150612 NN m1 m2 m4 m3 m3
  miarka2 miarka2 miarka2 miarka2 miarka2
zalecenia1 Not recommended zalecenia2 Acceptable zalecenia3 Recommended zalecenia4 Excellent

 

Turning operations
toczenie wzdluzne toczenie ksztaltowe
Straight turning Contour turning

 

stainless steel productivity speed
Respect recommended cutting speed during stainless steel machining To increase productivity it is recommended to increase speed while respecting Amax parameter

 

DesignationGradelsr
DNMG 110404 NN PL 10 11 4,76 0,4
DNMG 110408 NN PL 10 11 4,76 0,8
DNMG 150404 NN PL 10 15 4,76 0,4
DNMG 150408 NN PL 10 15 4,76 0,8
DNMG 150412 NN PL 10 15 4,76 1,2
DNMG 150604 NN PL 10 15 6,35 0,4
DNMG 150608 NN PL 10 15 6,35 0,8
DNMG 150612 NN PL 10 15 6,35 1,2

 

DNMG 110404 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,20 3,0 0,11 0,23 0,60 180 350 2,0 0,18
180 2,5 0,20 0,48 280
210 2,5 0,18 0,48 250
Alloy steel 2 180 0,20 2,5 0,11 0,20 0,48 120 280 2,0 0,15
230 2,5 0,20 0,40 250
280 0,20 2,0 0,09 0,18 0,40 210
320 2,0 0,16 0,32 180
High alloy steel 3 220 0,20 2,5 0,09 0,18 0,40 70 190 2,0 0,12
280 2,5 0,16 0,40 150
320 0,20 2,0 0,14 0,28 130
350 2,0 0,14 0,24 100
400 0,20 1,8 0,05 0,12 0,20 50 90 1,7 0,11
480 1,5 0,10 0,17 40 80 1,4 0,09
550 1,4 0,08 0,13 30 70 1,2 0,07
Austenitic stainless steel
 4 210 - 250 0,20 2,5 0,10 0,18 0,32 170 270 2,0 0,15
5 230 - 270 2,0 0,09 0,16 0,24 160 210 2,0 0,12
6 - 2,0 0,09 0,14 0,20 70 150 2,0 0,12
Ferritic stainless steel
 7 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,15
Martensitic stainless steel
 8 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,12
treated 120 190
Grey cast iron 9 140 - 230 0,20 3,0 0,08 0,20 0,64 170 250 2,0 0,18
0,60 230
0,60 210
Nodular cast iron 10 210 0,20 2,5 0,08 0,18 0,48 120 230 2,0 0,15
260 0,40 190
310 0,40 150
450 0,20 1,5 0,05 0,10 0,17 30 70 1,4 0,09
Nickel based alloys
 11 - 0,20 2,0 0,10 0,16 0,24 25 35 2,0 0,12
0,24 28 40
0,28 40 65
Titanium based alloys
 12 - 0,20 2,0 0,09 0,16 0,28 35 60 2,0 0,14
0,14 0,24 28 40 2,0 0,12

 

DNMG 110408 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,50 5,0 0,21 0,45 1,8 180 350 3,0 0,35
180 5,0 0,45 1,8 300
210 4,0 0,40 1,5 250
Alloy steel 2 180 0,50 5,0 0,21 0,40 1,2 120 280 3,0 0,30
230 4,0 0,40 1,2 250
280 0,50 4,0 0,18 0,35 1,2 210
320 3,5 0,35 1,0 180
High alloy steel 3 220 0,50 4,0 0,18 0,40 1,2 70 190 2,5 0,28
280 4,0 0,40 1,2 150
320 0,50 3,0 0,35 0,8 130
350 3,0 0,35 0,8 100
400 0,50 2,5 0,11 0,30 0,6 50 90 2,0 0,25
480 2,0 0,25 0,4 40 80 1,7 0,20
550 1,7 0,20 0,3 30 70 1,0 0,18
Austenitic stainless steel
 4 210 - 250 0,50 5,0 0,20 0,40 1,0 170 270 3,0 0,35
5 230 - 270 4,0 0,18 0,35 0,8 160 210 3,0 0,32
6 - 4,0 0,18 0,35 0,6 70 150 2,5 0,28
Ferritic stainless steel
 7 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
Martensitic stainless steel
 8 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
treated 120 190
Grey cast iron 9 140 - 230 0,50 5,0 0,15 0,60 2,0 170 250 3,0 0,35
1,8 230
1,8 210
Nodular cast iron 10 210 0,50 5,0 0,15 0,50 1,5 120 230 3,0 0,30
260 1,3 190
310 1,2 150
450 0,50 1,7 0,11 0,25 0,4 30 50 1,0 0,18
Nickel based alloys
 11 - 0,50 3,0 0,20 0,35 0,7 25 35 2,0 0,28
0,7 28 40
0,8 40 65
Titanium based alloys
 12 - 0,50 3,0 0,18 0,35 0,8 35 60 2,0 0,30
0,30 0,6 28 40 2,0 0,28

 

DNMG 150404 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,20 3,0 0,11 0,23 0,60 180 350 2,0 0,18
180 2,5 0,20 0,48 280
210 2,5 0,18 0,48 250
Alloy steel 2 180 0,20 2,5 0,11 0,20 0,48 120 280 2,0 0,15
230 2,5 0,20 0,40 250
280 0,20 2,0 0,09 0,18 0,40 210
320 2,0 0,16 0,32 180
High alloy steel 3 220 0,20 2,5 0,09 0,18 0,40 70 190 2,0 0,12
280 2,5 0,16 0,40 150
320 0,20 2,0 0,14 0,28 130
350 2,0 0,14 0,24 100
400 0,20 1,8 0,05 0,12 0,20 50 90 1,7 0,11
480 1,5 0,10 0,17 40 80 1,4 0,09
550 1,4 0,08 0,13 30 70 1,2 0,07
Austenitic stainless steel
 4 210 - 250 0,20 2,5 0,10 0,18 0,32 170 270 2,0 0,15
5 230 - 270 2,0 0,09 0,16 0,24 160 210 2,0 0,12
6 - 2,0 0,09 0,14 0,20 70 150 2,0 0,12
Ferritic stainless steel
 7 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,15
Martensitic stainless steel
 8 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,12
treated 120 190
Grey cast iron 9 140 - 230 0,20 3,0 0,08 0,20 0,64 170 250 2,0 0,18
0,60 230
0,60 210
Nodular cast iron 10 210 0,20 2,5 0,08 0,18 0,48 120 230 2,0 0,15
260 0,40 190
310 0,40 150
450 0,20 1,5 0,05 0,10 0,17 30 70 1,4 0,09
Nickel based alloys
 11 - 0,20 2,0 0,10 0,16 0,24 25 35 2,0 0,12
0,24 28 40
0,28 40 65
Titanium based alloys
 12 - 0,20 2,0 0,09 0,16 0,28 35 60 2,0 0,14
0,14 0,24 28 40 2,0 0,12

 

DNMG 150408 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,50 5,0 0,21 0,45 1,8 180 350 3,0 0,35
180 5,0 0,45 1,8 300
210 4,0 0,40 1,5 250
Alloy steel 2 180 0,50 5,0 0,21 0,40 1,2 120 280 3,0 0,30
230 4,0 0,40 1,2 250
280 0,50 4,0 0,18 0,35 1,2 210
320 3,5 0,35 1,0 180
High alloy steel 3 220 0,50 4,0 0,18 0,40 1,2 70 190 2,5 0,28
280 4,0 0,40 1,2 150
320 0,50 3,0 0,35 0,8 130
350 3,0 0,35 0,8 100
400 0,50 2,5 0,11 0,30 0,6 50 90 2,0 0,25
480 2,0 0,25 0,4 40 80 1,7 0,20
550 1,7 0,20 0,3 30 70 1,0 0,18
Austenitic stainless steel
 4 210 - 250 0,50 5,0 0,20 0,40 1,0 170 270 3,0 0,35
5 230 - 270 4,0 0,18 0,35 0,8 160 210 3,0 0,32
6 - 4,0 0,18 0,35 0,6 70 150 2,5 0,28
Ferritic stainless steel
 7 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
Martensitic stainless steel
 8 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
treated 120 190
Grey cast iron 9 140 - 230 0,50 5,0 0,15 0,60 2,0 170 250 3,0 0,35
1,8 230
1,8 210
Nodular cast iron 10 210 0,50 5,0 0,15 0,50 1,5 120 230 3,0 0,30
260 1,3 190
310 1,2 150
450 0,50 1,7 0,11 0,25 0,4 30 50 1,0 0,18
Nickel based alloys
 11 - 0,50 3,0 0,20 0,35 0,7 25 35 2,0 0,28
0,7 28 40
0,8 40 65
Nickel based alloys
 12 - 0,50 3,0 0,18 0,35 0,8 35 60 2,0 0,30
0,30 0,6 28 40 2,0 0,28

 

DNMG 150412 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,50 5,0 0,27 0,68 3,1 180 330 4,0 0,50
180 5,0 0,68 3,1 280
210 5,0 0,60 2,6 250
Alloy steel 2 180 0,50 5,0 0,27 0,60 2,6 120 280 4,0 0,45
230 5,0 0,60 2,0 250
280 5,0 0,23 0,53 2,0 210
320 4,0 0,53 1,7 180
High alloy steel 3 220 0,50 5,0 0,23 0,60 2,0 70 190 4,0 0,40
280 5,0 0,60 2,0 150
320 4,0 0,53 1,6 130
350 4,0 0,53 1,6 100
400 0,50 3,5 0,14 0,45 1,2 50 90 3,4 0,36
480 3,0 0,35 0,9 40 80 2,9 0,30
550 2,5 0,28 0,6 30 70 2,5 0,25
Austenitic stainless steel
 4 210 - 250 0,50 5,0 0,26 0,52 1,7 170 270 4,0 0,40
5 230 - 270 5,0 0,23 0,46 1,4 160 210 4,0 0,36
6 - 5,0 0,23 0,46 1,0 70 150 4,0 0,32
Ferritic stainless steel
 7 annealed 0,50 5,0 0,29 0,46 1,5 170 250 4,0 0,35
Martensitic stainless steel
 8 annealed 0,50 5,0 0,29 0,46 1,5 170 250 4,0 0,35
treated 120 190
Grey cast iron 9 140 - 230 0,50 5,0 0,20 0,90 3,0 170 250 4,0 0,60
2,7 230
2,7 210
Nodular cast iron 10 210 0,50 5,0 0,20 0,70 2,3 120 230 4,0 0,50
260 2,0 190
310 1,8 150
450 0,50 1,8 0,06 0,15 0,3 30 70 1,2 0,12
Nickel based alloys
 11 - 0,50 5,0 0,26 0,46 1,4 25 35 3,0 0,38
1,4 28 40
1,6 40 65
Titanium base alloys
 12 - 0,50 5,0 0,23 0,46 1,6 35 60 3,0 0,38
0,39 1,2 28 40 3,0 0,32

 

DNMG 150604 NN
Material groupGroup materialBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,20 3,0 0,11 0,23 0,60 180 350 2,0 0,18
180 2,5 0,20 0,48 280
210 2,5 0,18 0,48 250
Alloy steel 2 180 0,20 2,5 0,11 0,20 0,48 120 280 2,0 0,15
230 2,5 0,20 0,40 250
280 0,20 2,0 0,09 0,18 0,40 210
320 2,0 0,16 0,32 180
High alloy steel 3 220 0,20 2,5 0,09 0,18 0,40 70 190 2,0 0,12
280 2,5 0,16 0,40 150
320 0,20 2,0 0,14 0,28 130
350 2,0 0,14 0,24 100
400 0,20 1,8 0,05 0,12 0,20 50 90 1,7 0,11
480 1,5 0,10 0,17 40 80 1,4 0,09
550 1,4 0,08 0,13 30 70 1,2 0,07
Austenitic stainless steel
 4 210 - 250 0,20 2,5 0,10 0,18 0,32 170 270 2,0 0,15
5 230 - 270 2,0 0,09 0,16 0,24 160 210 2,0 0,12
6 - 2,0 0,09 0,14 0,20 70 150 2,0 0,12
Ferritic stainless steel
 7 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,15
Martensitic stainless steel
 8 annealed 0,20 2,0 0,11 0,18 0,28 170 250 2,0 0,12
treated 120 190
Grey cast iron 9 140 - 230 0,20 3,0 0,08 0,20 0,64 170 250 2,0 0,18
0,60 230
0,60 210
Nodular cast iron 10 210 0,20 2,5 0,08 0,18 0,48 120 230 2,0 0,15
260 0,40 190
310 0,40 150
450 0,20 1,5 0,05 0,10 0,17 30 70 1,4 0,09
Nickel based alloys
 11 - 0,20 2,0 0,10 0,16 0,24 25 35 2,0 0,12
0,24 28 40
0,28 40 65
Titanium based alloys
 12 - 0,20 2,0 0,09 0,16 0,28 35 60 2,0 0,14
0,14 0,24 28 40 2,0 0,12

 

DNMG 150608 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,50 5,0 0,21 0,45 1,8 180 350 3,0 0,35
180 5,0 0,45 1,8 300
210 4,0 0,40 1,5 250
Alloy steel 2 180 0,50 5,0 0,21 0,40 1,2 120 280 3,0 0,30
230 4,0 0,40 1,2 250
280 0,50 4,0 0,18 0,35 1,2 210
320 3,5 0,35 1,0 180
High alloy steel 3 220 0,50 4,0 0,18 0,40 1,2 70 190 2,5 0,28
280 4,0 0,40 1,2 150
320 0,50 3,0 0,35 0,8 130
350 3,0 0,35 0,8 100
400 0,50 2,5 0,11 0,30 0,6 50 90 2,0 0,25
480 2,0 0,25 0,4 40 80 1,7 0,20
550 1,7 0,20 0,3 30 70 1,0 0,18
Austenitic stainless steel
 4 210 - 250 0,50 5,0 0,20 0,40 1,0 170 270 3,0 0,35
5 230 - 270 4,0 0,18 0,35 0,8 160 210 3,0 0,32
6 - 4,0 0,18 0,35 0,6 70 150 2,5 0,28
Ferritic stainless steel
 7 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
Martensitic stainless steel
 8 annealed 0,50 4,0 0,22 0,35 0,9 170 250 3,0 0,32
treated 120 190
Grey cast iron 9 140 - 230 0,50 5,0 0,15 0,60 2,0 170 250 3,0 0,35
1,8 230
1,8 210
Nodular cast iron 10 210 0,50 5,0 0,15 0,50 1,5 120 230 3,0 0,30
260 1,3 190
310 1,2 150
450 0,50 1,7 0,11 0,25 0,4 30 50 1,0 0,18
Nickel based alloys
 11 - 0,50 3,0 0,20 0,35 0,7 25 35 2,0 0,28
0,7 28 40
0,8 40 65
Titanium based alloys
 12 - 0,50 3,0 0,18 0,35 0,8 35 60 2,0 0,30
0,30 0,6 28 40 2,0 0,28

 

DNMG 150612 NN
Material groupGroup numberBrinell hardness
[HB]		ap [mm]Feed [mm/turn]A max [mm2]Vc [m/min]Optimal cutting conditions
minmaxminmaxminmaxapfeed
Low carbon steel 1 150 0,50 5,0 0,27 0,68 3,1 180 330 4,0 0,50
180 5,0 0,68 3,1 280
210 5,0 0,60 2,6 250
Alloy steel 2 180 0,50 5,0 0,27 0,60 2,6 120 280 4,0 0,45
230 5,0 0,60 2,0 250
280 5,0 0,23 0,53 2,0 210
320 4,0 0,53 1,7 180
High alloy steel 3 220 0,50 5,0 0,23 0,60 2,0 70 190 4,0 0,40
280 5,0 0,60 2,0 150
320 4,0 0,53 1,6 130
350 4,0 0,53 1,6 100
400 0,50 3,5 0,14 0,45 1,2 50 90 3,4 0,36
480 3,0 0,35 0,9 40 80 2,9 0,30
550 2,5 0,28 0,6 30 70 2,5 0,25
Austenitic stainless steel
 4 210 - 250 0,50 5,0 0,26 0,52 1,7 170 270 4,0 0,40
5 230 - 270 5,0 0,23 0,46 1,4 160 210 4,0 0,36
6 - 5,0 0,23 0,46 1,0 70 150 4,0 0,32
Ferritic stainless steel
 7 annealed 0,50 5,0 0,29 0,46 1,5 170 250 4,0 0,35
Martensitic stainless steel
 8 annealed 0,50 5,0 0,29 0,46 1,5 170 250 4,0 0,35
treated 120 190
Grey cast iron 9 140 - 230 0,50 5,0 0,20 0,90 3,0 170 250 4,0 0,60
2,7 230
2,7 210
Nodular cast iron 10 210 0,50 5,0 0,20 0,70 2,3 120 230 4,0 0,50
260 2,0 190
310 1,8 150
450 0,50 1,8 0,06 0,15 0,3 30 70 1,2 0,12
Nickel based alloys
 11 - 0,50 5,0 0,26 0,46 1,4 25 35 3,0 0,38
1,4 28 40
1,6 40 65
Titanium based alloys
 12 - 0,50 5,0 0,23 0,46 1,6 35 60 3,0 0,38
0,39 1,2 28 40 3,0 0,32